PC台湾奇美PC-110
| 曲模量(弯曲弹性率) | ASTM D790/ISO 178 | 24000 | kg/cm2(MPa)[Lb/in2] | ||
| 弯曲强度 | ASTM D790/ISO 178 | 920 | kg/cm2(MPa)[Lb/in2] | ||
| 洛氏硬度 | ASTM D785 | M-77 | |||
| IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | 15 | kg·cm/cm(J/M)ft·lb/in | |
| 1/4" -30℃ | ASTM D256/ISO 179 | -- | kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" 23℃ | ASTM D256/ISO 179 | 87 | kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" -30℃ | ASTM D256/ISO 179 | -- | kg·cm/cm(J/M)ft·lb/in | ||
| Charpy冲击强度 | 23℃ （缺口） | ASTM D256/ISO 179 | -- | kg·cm/cm(J/M)ft·lb/in | |
| -30℃（缺口） | ASTM D256/ISO 179 | -- | kg·cm/cm(J/M)ft·lb/in | ||
| 23℃（无缺口） | ASTM D256/ISO 179 | -- | kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（无缺口） | ASTM D256/ISO 179 | -- | kg·cm/cm(J/M)ft·lb/in | ||
| 物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 1.2 | ||
| 成型收缩率 | ASTM D955 | 0.5-0.7 | % | ||
| 熔融指数（流动系数） | 200℃/5kg | ASTM D1238/ISO 1133 | （300℃.1.2kg）,10 | g/10min | |
| 220℃/10kg | ASTM D1238/ISO 1133 | -- | g/10min | ||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 0.20 | % | ||
| 热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | 136 | ℃（℉） |
| 未退火 | ASTM D648/ISO 75 | 125 |